Magnesia Chrome Brick is a kind of basic refractory material with more than 90% magnesium oxide content and periclase as the main crystal phaseis. For the Magnesia Chrome Brick, the maximum allowed environment temperature is 1700℃. It has features of high strength, high refractoriness under load, high alkali erosion resistance and high thermal shock resistance under the load conditions of 1500~1650℃ and also have big advantages of environmental protection and long service life.
It is mainly divided into common magnesia chrome brick、direct-bonded magnesia chrome brick、re-bonded magnesia chrome brick、semi-re-bonded magnesia chrome brick.

Technical Data

Item Commom Magnesia Chrome Brick Direct-Bonded Magnesia Chrome Brick
Model MGe6 MGe8 MGe12 MGe16 DMGe4 DMGe8 DMGe12 DMGe16
MgO % 80 72 70 65 85 77 74 69
Cr2O3 % 7 10 13 17 5.5 9.1 14 18
CaO % 1.2 1.2 1.2 1.2 1.1 1.4 1.2 1.2
SiO2 % 3.4 4 4 4.2 1.3 1.2 1.2 1.5
Al2O3 % 4.5 6.5 6 6 3.5 4 3.5 4.5
Fe2O3 % 4 4.8 5.5 6.5 3 6.4 5 5.7
Apparent Porosity % 17 18 18 18 18 18 18 18
Bulk Density g/cm3 3 3 3.02 3.05 3.02 3.04 3.06 3.08
Cold Crushing Strength Mpa 55 55 55  50 50 50 55  55
Refractoriness Under Load °C  1600  1600  1600  1600  1700  1700  1700  1700
Thermal expansion % 1000°C / / / / 1  1  1  0.9
Thermal expansion % 1600°C / / / / 1.8  1.8  1.8  1.6
Item Fused Semi-rebond Magnesia Chrome Brick Fused Rebonded Magnesia Chrome Brick
Model SRMGe-16 SRMGe-18 SRMGe-20 SRMGe-22 SRMGe-26 RMGe-12 RMGe-14
MgO % 68 64 65 56 56 75 75
Cr2O3 % 16 18 20 22 26 12 14
SiO2 % 1.5 1.5 1 2.5 2.5 1.5 1.5
Apparent Porosity % 16 16 14 16 16 15 15
Bulk Density g/cm3 3.1 3.1 3.1 3.1 3.1 3.2 3.2
Cold Crushing Strength Mpa 40 40 40 40 40 50 50
Refractoriness Under Load °C 1700 1700 1700 1700  1700  1700  1700

Application

It is mainly used for steelmaking basic open-hearth furnace, electric furnace bottom and wall, permanent lining of oxygen converter, non-ferrous metal metallurgy furnace, high-temperature tunnel kiln, lining of rotary kiln, furnace bottom and wall of heating furnace, regenerative chamber of glass furnace and etc.