Product Introduction
Mullite Refractory Brick is a kind of High-aluminum refractories that regard the mullite (Al2O3•SiO2) as the main crystal phase. The average alumina content is between 65% and 75%. In addition to mullite mineral composition, which contains lower alumina also contains a small amount of glass and cristobalite; higher alumina containing a small amount of corundum. High refractoriness up to 1790°C. Load softening starting temperature 1600 ~ 1700 °C. Room temperature compressive strength 70 ~ 260MPa. Good thermal shock resistance.
Technical Data
| Item | MU 60 | MU 65 | MU 70 | MU 75 | |
| Chemical composition | Al2O3 | ≥60 | ≥65 | ≥70 | ≥75 |
| SiO2 | ≤35 | ≤33 | ≤26 | ≤24 | |
| Fe2O3 | ≤1.0 | ≤1.0 | ≤0.6 | ≤0.4 | |
| Apparent Porosity％ | ≤17 | ≤17 | ≤17 | ≤18 | |
| Bulk Density g/cm3 | ≥2.55 | ≥2.55 | ≥2.55 | ≥2.55 | |
| Cold Crushing Strength Mpa | ≥60 | ≥60 | ≥80 | ≥80 | |
| 0.2Mpa Refractoriness Under Load T0.6 ℃ | ≥1580 | ≥1600 | ≥1600 | ≥1650 | |
| Permanent Linear Change On Reheating （%）1500℃X2h | 0～+0.4 | 0～+0.4 | 0～+0.4 | 0～+0.4 | |
| Thermal Shock Resistances 100℃ water cycles | ≥18 | ≥18 | ≥18 | ≥18 | |
| 20－1000℃ Thermal Expansich10-6/℃ | 0.6 | 0.6 | 0.6 | 0.55 | |
| Thermal Conductivity (W/MK) 1000℃ | 1.74 | 1.84 | 1.95 | 1.95 | |
Application
The mullite brick adopts the imported plate corundum and high-purity fused corundum as the main raw materials, and adopts advanced ultrafine powder addition technology. After mixing, drying and forming, it is fired in a high-temperature shuttle kiln. So Mullite bricks are widely used in slag gasification furnaces, synthetic ammonia conversion furnaces, carbon black reactors, and refractory kiln furnaces, Furnace roof of hot blast stove, Furnace stack and bottom of blast furnace,Regenerative chamber of glass melting furnace and Ceramic high temperature furnace.