Product Introduction
High alumina cement is an excellent unshaped refractory material for sale in Rongsheng Company, whose main chemical composition of High Alumina Cement includes calcium aluminate, plus about 50% of the alumina.High alumina brick is called bauxite cement before ,Which is a kind of hydraulic binder, being produced after the calcining and grinding with the bauxite and limestone as the raw material. So high alumina cement is also called calcium aluminate cement.
High Alumina Cement is mainly manufacturered by rotary kiln sintering, arc furnace melting method and reverberatory furnace melting method, etc.
Technical Data
| High Alumina Cement | ||||||
| Cement Model | CA-65 | CA-68 | CA-70 | CA-75 | CA-80 | |
| Chemical Composition (%) | Al2O3 | 64-66 | 67-69 | 69-71 | 73-75 | 77-80 |
| CaO | 32-34 | 29-31 | 27-29 | 23-25 | 18-20 | |
| SiO2 | 1.8 | 1.2 | 0.3 | 0.3 | 0.3 | |
| Fe2O3 | 0.6 | 0.6 | 0.3 | 0.3 | 0.3 | |
| Specific Surface (cm2/g) | 4500 | 4500 | 5000 | 5500 | 7000 | |
| Setting time (h:min) | Initial setting (min) | 0:40 | 0:40 | 0:40 | 0:45 | 0:45 |
| Final Setting (min) | 8:00 | 8:00 | 10:00 | 10:00 | 10:00 | |
| Cold Modulus of Rupture (MPa) | 24 hour | 6.0min | 6.0min | 6.0min | 6.0min | 5.0min |
| 72 hour | 8.0min | 8.0min | 8.0min | 8.0min | 6.0min | |
| Cold Crushing Strength (Mpa) | 24hour | 45.0min | 45.0min | 45.0min | 45.0min | 35.0min |
| 72hour | 70.0min | 70.0min | 70.0min | 70.0min | 60.0min | |
| Refractoriness (°C) | 1680 | 1710 | 1730 | 1750 | 1770 | |
Application Of High Alumina Cement
1. It is particularly suitable for furnace shells, high-temperature pipes, blast furnaces, electric furnaces, and high-temperature environments such as steel plants and aluminum plants.
2. In the chemical industry, it is widely used for corrosion-resistant linings of equipment and pipelines in fertilizer plants, refineries, chemical plants, etc.
3. High-alumina cement is the main raw material for the production of various refractory castables, refractory bricks and other refractory materials.